CO₂激光单点修复对光束焦斑能量损失的影响

1.
Research Center of Laser Fusion,CAEP,P.O.Box 919-988,Mianyang 621900,China;
2.
Department of Physic Electronics,University of Electronic Science and Technology of China,Chengdu 610054,China

摘要: 利用模拟美国国家点火装置（NIF）终端光学组件光路排布的检测平台，测试了熔石英光学元件表面不同尺寸、不同密度修复坑对光束焦斑能量所造成的影响。实验结果表明，在修复坑密度较小时，能量损失率和修复坑密度呈线性相关，密度达到一定值后则达到饱和，修复坑尺寸对能量损失率随密度的增长速度造成影响，修复坑尺寸越大，能量损失率随密度的增长越快。按照NIF装置3%束间功率平衡的技术指标，要求修复坑密度必须控制在2 cm-2以下。
- CO2激光 /
- 熔石英 /
- 修复 /
- 能量损失 /
- 焦斑
Abstract: An experimental setup referring to the optical element configuration of National Ignition Facility was built. The energy loss from mitigation cone by CO2 laser was tested. The results showed that the loss ratio had a linear correlation with the density of mitigation cone while the density was low. The energy would lose faster with the increase of density if the mitigation cone was larger. Density of mitigation cone must be small than 2 cm-2 to ensure the loss ratio less than 3%.
- CO2 laser /
- fused silica /
- mitigation /
- energy loss /
- focal spot

1.	陈金宝，相广彪，王小林，张汉伟，张江彬，华卫红. 低辐照剂量率下光纤激光器输出功率的自漂白-辐照平衡实验研究. 强激光与粒子束. 2024(12): 5-7 . 本站查看
2.	王世杰，蔡一鸣，张志伦，林贤峰，邢颍滨，廖雷，李进延. 自研100μm/400μm光纤实现1000W纳秒脉冲激光输出. 中国激光. 2021(01): 206-209 . 百度学术
3.	王世杰，张志伦，曹驰，林贤峰，邢颍滨，廖雷，李进延. 利用国产光纤实现平均功率761W、脉冲能量17.5mJ纳秒脉冲激光输出. 中国激光. 2019(12): 316-319 . 百度学术
4.	许阳，房强，谢兆鑫，李锦辉，崔雪龙，史伟. 基于915nm半导体激光单端前向抽运的单纤准单模2kW全光纤激光振荡器. 中国激光. 2018(04): 44-48 . 百度学术