沉积温度对HfO2薄膜残余应力的影响
Influences of deposition temperature on residual stress of HfO2 films
-
摘要: 用电子束蒸发方法制备了HfO2薄膜，根据镀膜前后基片曲率半径的变化，用Stoney公式计算了薄膜应力，讨论了沉积温度对薄膜残余应力的影响。结果发现，HfO2薄膜的残余应力均为张应力，应力值随沉积温度的升高先增大后减小，在280 ℃左右出现极大值。对样品进行了XRD测试，从微观结构上对实验结果进行了分析，发现微结构演变引起的内应力变化是引起薄膜残余应力改变的主要因素，HfO2薄膜在所选沉积温度60~350 ℃内出现了晶态转变，堆积密度随温度升高而增大。Abstract: HfO2 films were prepared by electron beam evaporation. The residual stress was measured by ZYGO interferometer. The results showed that the residual stresses of HfO2 films were tensile and increased with the increase of deposition temperature firstly, then decreased. The microstructure of the HfO2 films was inspected with X-ray diffraction (XRD). The microstructure of the films transmitted from amorphous to polycrystalline, which corresponded to the variation of the residual stress. The microstructure of HfO2 film changed as the deposition temperature increased and the residual stress evolved as the changing of the microstructure.
-
Key words:
- hfo2 films /
- residual stress /
- deposition temperature /
- microstructure /
- xrd
-
点击查看大图
计量
- 文章访问数: 2828
- HTML全文浏览量: 292
- PDF下载量: 835
- 被引次数: 0
下载: