yang anmin, xia liansheng, wang hui, et al. Emission characteristic of scandate cathode with large diameter[J]. High Power Laser and Particle Beams, 2011, 23.
Citation:
yang anmin, xia liansheng, wang hui, et al. Emission characteristic of scandate cathode with large diameter[J]. High Power Laser and Particle Beams, 2011, 23.
yang anmin, xia liansheng, wang hui, et al. Emission characteristic of scandate cathode with large diameter[J]. High Power Laser and Particle Beams, 2011, 23.
Citation:
yang anmin, xia liansheng, wang hui, et al. Emission characteristic of scandate cathode with large diameter[J]. High Power Laser and Particle Beams, 2011, 23.
In order to acquire Kilo-Ampere level emission current, a 100 mm diameter scandate cathode was manufactured. A 2 MV injector test stand was established with a large area thermionic cathode. A 1 038 A emission current was produced with a diode voltage 1.95 MV, pulse width 120 ns(FWHM), cathode temperature 1 120 ℃.The emission current density was 13 A/cm2. The results indicate that the ability of cathode emission relies on diode vacuum and cathode activation temperature.